lnvestigation for corrosion behavior of ferritic core materials in CO gas cooled reactor

; ; Mizuta, Shunji

JNC TN9400 2000-040, 41 Pages, 2000/03

JNC-TN9400-2000-040.pdf:0.85MB

The corrosion behavior of ferritic stainless steels applied to core components under C0 gas environment was investigated in order to be helpful to fuel design in C0 gas cooled reactor as the feasibility study for fast breeder reactor. The dependence of the corrosion behavior, before a breakaway occurs, on C0 gas temperature, Si and Cr contents of ferritic steels was determined quantitatively. The following correlations to calculate the metal loss thickness was established. X = 4.4w w = √(kt) k = exp( - 5.45[Si]) exp( - 1.09[Cr]) exp( - 11253/T) = 1.65 104.40 10 X : metal loss thickness[ml, w : corrosion weight gain [mg/cm] k : parabola constant [(mg/cm)/hr], t : time [hr], : constant [Si] : Si content[wt.%], [Cr] : Cr content [wt.%], T : temperature [K]

Corrosion tests of cladding inner surface coating

*

PNC TJ9605 91-001, 28 Pages, 1990/10

PNC-TJ9605-91-001.pdf:1.81MB

The present report describes the results of studies performed sa a part of the results of "CORROSION TESTS OF CLADDING INNER SURFACE COATING" during a period of Feb. 20 - Mar.30, 1990. In the present study, corrosion tests have been carried out with CsOH to evaluate corrosion resistance of ferritic stainless steel and coated stainless steel. The following results were drawn from the present study (1)Corrosion tests of austenitic and ferritic stainless steel with ScOH were made at temperatures of 500-700C. After corrosin tests, intergranular attack was found to occur in the austenitic steel, however, there was no intergranular attack in the ferritic steel. Ferritic steel appears to have corrosion resistance to liquid CsOH superior to austenitic steel. (2)Corrosion tests between Ni-Ti, Ti, Al coatings on stainless steel and CsOH were made at temperature of 500-700C. Ni-Ti and Al coated stainless steel showed no intergranular attack, though the coatings were locally detached from the stainless stell substrates. Intergranular attack was observed in the Ti coated stainless steel. Ni-Ti and Al coating seem to be useful for reduction of intergranular attack of stainless steel cladding.

Corrosion estimation of sheath materials using signal cables under light water reactor severe accident environment

Nakano, Hiroko; Shibata, Hiroshi; Takeuchi, Tomoaki; Matsui, Yoshinori; Tsuchiya, Kunihiko

no journal, , 

no abstracts in English